15-53um WC-17Co Agglomerated and sintered powder

GP17-1 WC-17Co Tungsten Carbide Powder Agglomerated and sintered 15-53um Tungsten Carbides is generally best using High Velocity Oxygen Fuel HVOF Tungsten Carbide Coating spray. This powder offers wonderful bonding strength and impact toghness; Excellent sliding resistance, shock resistance, wear resistance and durable erosion resistance; Maximum Tungsten Carbide Coating operating temperature is 500℃, Mainly used for Papermaking Rolls, Turbine, Compressor Blades. With Excellent toughness of coating.

The powder is composed of two main components: tungsten carbide (WC) and cobalt (Co). Tungsten carbide is a very hard and durable material that provides high wear resistance, while cobalt acts as a binder to hold the tungsten carbide particles together.

15-53um WC-17Co Agglomerated and sintered powder refers to a type of powder material that is composed of tungsten carbide (WC) particles and a cobalt (Co) binder. The powder particles have a size range of 15 to 53 micrometers (um). The powder is agglomerated, meaning that the individual particles are bonded together to form larger clusters. It is then sintered, a process where the powder is heated to a high temperature to fuse the particles together, resulting in a solid material. This type of powder is commonly used in applications that require high hardness and wear resistance, such as cutting tools, wear parts, and metal forming dies. The cobalt binder helps to provide toughness and strength to the material.

Spray System HVOF/HVAF/APS

Coating Micro-hardness 950-1300 HV0.3

Bonding Strength  ≥70MPa

Porosity ＜1%

Deposit Efficiency  45-65%

Maximum Service Temperature

  500℃

Product Categories : Thermal Spray Materials > Tungsten Carbide Powder