Thermal Spray Powder HVOF Coating properties:
Thermal Spray Coating service
Cr3C2-NiCr coating properties are influenced significantly by the spray process and spray parameters.
The abrasive wear rate for the chromium carbide coatings is controlled by several factors such as:
the morphology of the starting powder,the size and distribution of the chrome carbide particles,the hardness of the chromium carbide particles relative to the abrasive particles
the properties of the matrix and its volume fraction, and,the coating process, which determines the coating characteristics such as:
Phase composition,Density,Hardness,Bond strength and,The residual stresses
Typical Properties of the Chrome Carbide Coating
Apparent metallographic porosity
<1.0%
Cr3C2-25NiCr, 2-25um Chromium Carbide Powder is generally best using HVOF spray. This powder offers a dense coating that has excellent corrosion resistance, and maximum operating temperature is 870 °C . It mainly used for hydraulic rod repair,pump rod repair,valve parts repair, , and steel rollers repair etc. The manufacturing process is Agglomerated and Sintered which can bring coating a better deposit efficiency and micro-hardness.
Bond strength to steel 70 MPa 500µm 10,000 PSI
Coating hardness, HV300
950-1,100
Typical as-sprayed roughness Ra, micro-inch
2-3.2 µm
80-120 µinch
Maximum coating thickness
1 mm
Maximum working temperature
750°C
Product Categories : Thermal Spray Materials > Chromium Carbide Powder
75Cr3C2-25NiCr Thermal Spray Powder 20-53um
75Cr3C2-25NiCr Thermal Spray Powder 45-90um
75Cr3C2-25NiCr HVOF Powder 15-45um
Chromium Carbides powder Cr3C2-20NiCr 15-45um
80Cr3C2-20NiCr Thermal Spray Powder 15-45um
15-38um Cr3C2-25NiCr Thermal Spray Powders
Cr3C2-37WC-18NiCoCr Thermal Spray Powder HVOF 15-45um
75Cr3C2-25NiCr Thermal Spray Powder 5-25um